316 316Dr di-staen L a 316H: Beth yw'r gwahaniaethau rhyngddynt?
316 316Dr di-staen L a 316H: Beth yw'r gwahaniaethau rhyngddynt?
Mae'r prif wahaniaeth yn gorwedd yn y cynnwys carbon, sy'n pennu defnydd sylfaenol pob gradd dur di-staen: mae gan 316L y cynnwys carbon isaf (< 0.03%), making it ideal for welding applications because it exhibits good corrosion resistance after welding; 316H has the highest carbon content (0.04-0.10%), giving it higher strength and creep resistance at high temperatures; while standard 316 has an even higher upper limit for carbon content (0.08%), falling in between the two, but due to its carbon content, it cannot obtain dual certification as both 316L and 316H.
Beth mae 316H yn ei olygu?
Priodweddau Cyffredinol
Mae aloi 316H (UNS S31609) yn aloi carbon uchel wedi'i addasu o aloi 316, a ddatblygwyd yn benodol ar gyfer amgylcheddau tymheredd uchel. Mae'r aloi hwn yn arddangos cryfder uwch ar dymheredd uchel ac mae'n addas ar gyfer cydrannau strwythurol a llestri pwysau sy'n gweithredu ar dymheredd uwch na 932 gradd F (500 gradd).
Mae dur gwrthstaen 316 yn ddur di-staen molybdenwm-sy'n cynnwys cromiwm austenitig-nicel. Mae ychwanegu molybdenwm yn gwella ei ymwrthedd cyrydiad, yn gwella ei wrthwynebiad i gyrydiad tyllu o doddiannau clorid, ac yn cynyddu ei gryfder tymheredd uchel. Ac eithrio cryfder tymheredd uchel ychydig yn uwch na 304 o ddur di-staen, mae ei briodweddau yr un fath yn y bôn â 304 o ddur di-staen, mae dur di-staen yn dangos ymwrthedd cyrydiad gwell, yn enwedig yn erbyn asid sylffwrig, asid hydroclorig, asid asetig, asid fformig, asid tartarig, sylffadau asidig, a chloridau sylfaenol.
Mae dur di-staen 316L yn ddur di-staen isel-carbon austenitig-nicel gyda'r un ymwrthedd cyrydiad â 316 o ddur di-staen, ond mae ganddo ymwrthedd cryfach i gyrydiad rhyng-gronynnog ar ôl weldio.
Mae dur di-staen 316H yn fersiwn carbon uchel o 316 o ddur di-staen, sy'n fwy addas ar gyfer amgylcheddau tymheredd uchel. Mae gan ddur di-staen 316Ti cytbwys briodweddau tebyg. Mae'r cynnwys carbon uwch yn rhoi cryfder tynnol uwch a chryfder cynnyrch. Mae strwythur austenitig y deunydd hwn hefyd yn rhoi caledwch rhagorol iddo, hyd yn oed ar dymheredd isel.
Tabl Cymharu
Mae'r tabl isod yn crynhoi'r prif wahaniaethau rhwng dur di-staen 316, 316L, a 316H.
| Eiddo/Nodwedd | 316 Dur Di-staen | 316L Dur Di-staen | 316H Dur Di-staen |
|---|---|---|---|
| Cynnwys Carbon (uchafswm) | 0.08% | 0.03% | 0.04–0.10% |
| Gwrthsefyll Cyrydiad | Ardderchog | Ardderchog (gorau ar ôl weldio) | Ardderchog |
| Weldability | Da (efallai y bydd angen postio-weldio anelio) | Ardderchog (dim angen anelio) | Da (llai na 316L) |
| -Cryfder Tymheredd Uchel | Da | Cymedrol | Ardderchog |
| Defnyddiau Nodweddiadol | Prosesu cemegol, rhannau morol | Tanciau fferyllol, bwyd, weldio | Boeleri, cyfnewidwyr gwres |
| Safonau Perthnasol | ASTM A312, A240, A182 | ASTM A312, A240, A182 | ASTM A312, A240, A182 |
| Priodweddau Mecanyddol | Cryfder uchel | Cryfder ychydig yn is | Uchaf ar adegau uchel |
Cyfansoddiad Cemegol %
| Gradd | C | Si | P | S | Cr | Mn | Ni | Cu | Mo | Ti | Fe |
| aloi 316 | 0.08 uchafswm | 0.75 uchafswm | 0.045 uchafswm | 0.030 uchafswm | 16.0 - 18.0 | 2.0 uchafswm | 10.0 - 14.0 | - | 2.0 - 3.0 | - | Gweddill |
| Aloi 316L | 0.03 uchafswm | 0.75 uchafswm | 0.045 uchafswm | 0.030 uchafswm | 16.0 - 18.0 | 2.0 uchafswm | 10.0 - 14.0 | - | 2.0 - 2.0 | - | Gweddill |
| Aloi 316H | 0.04 - 0.10 | 0.75 uchafswm | 0.045 uchafswm | 0.030 uchafswm | 16.0 - 18.0 | 2.0 uchafswm | 10.0 - 14.0 | - | 2.0 - 3.0 | - | Gweddill |
Priodweddau Corfforol
| Unedau | Tymheredd mewn gradd | |
| Dwysedd | 7.99 g / cm³ | Ystafell |
| Gwres Penodol | 0.12 Kcal/kg.C | 22 gradd |
| Ystod Toddi | 1371 - 1421 gradd | - |
| Modwlws Elastigedd | 193 KN/mm² | 22 gradd |
| Gwrthiant Trydanol | 74 µΩ.cm | Ystafell |
| Cyfernod Ehangu | 16.0 µm/m gradd | 20 - 100 gradd |
| Dargludedd Thermol | 16.2 W/m - gradd K | 100 gradd |
| Nodwedd | 316 Dur Di-staen | 316L Dur Di-staen | 316H Dur Di-staen |
|---|---|---|---|
| Cynnwys Carbon | Llai na neu'n hafal i 0.08% | Llai na neu'n hafal i 0.03% | 0.04 – 0.10% |
| Defnydd Cynradd | Pwrpas cyffredinol, cydbwysedd eiddo | Strwythurau wedi'u weldio, amgylcheddau sy'n dueddol o rydu ar ôl dod i gysylltiad â gwres | Cymwysiadau-tymheredd uchel, llestri gwasgedd |
| Mantais Allweddol | Gwrthiant cyrydiad da | Weldadwyedd ardderchog a gwrthiant cyrydiad ar ôl weldio | Cryfder uchel a gwrthiant ymgripiad ar dymheredd uchel |
| Weldability | Da, ond mae angen triniaeth wres ar ôl-weldio mewn rhai achosion | Ardderchog, yn ddelfrydol ar gyfer weldio | Yn agored i sensiteiddio os caiff ei ddal yn yr ystod 450-850 gradd |
Mae Gnee Steel yn arbenigo mewn cynhyrchu ystod eang o gynhyrchion dur di-staen. Mae pecynnu cynnyrch Gnee Steel yn cynnwys: Strapio Dur: Mae pibellau â diamedr allanol o 3 modfedd neu lai fel arfer yn cael eu strapio ynghyd â ffilm polypropylen i atal rhwd yn ystod llongau cefnfor, ac yna'n cael eu diogelu â strapio dur. Casys / Cewyll Pren: Mae pibellau fel arfer yn cael eu pecynnu mewn casys pren neu gewyll i amddiffyn y pibellau wrth eu cludo, yn enwedig y rhai sy'n hirach neu sydd â diamedrau mwy. Pecynnu Allforio Seaworthy: Mae cyflenwyr fel arfer yn defnyddio dulliau pecynnu allforio safonol sy'n addas i'r môr, a all gynnwys amrywiaeth o ddeunyddiau a thechnegau i amddiffyn y pibellau wrth eu cludo. Pecynnu Tarpolin: Mae hyn yn atal glaw, dŵr môr, a ffactorau allanol eraill rhag treiddio i'r cewyll allforio wrth eu cludo. Mae Gnee Steel yn arbenigo mewn cynhyrchu a gwerthu deunyddiau aloi. Defnyddir cynhyrchion Gnee Steel yn eang yn y sectorau awyrofod, cemegol, pŵer, modurol ac ynni niwclear, a gallwn ddarparu atebion deunydd aloi wedi'u haddasu yn seiliedig ar anghenion cwsmeriaid. Ar gyfer prisio deunydd aloi neu atebion deunydd aloi wedi'u haddasu, cysylltwch â ni am ddyfynbris:ru@gneesteelgroup.com